Three phenolic groups
Efficient radical scavenging per unit weight.
SUNNOX® CA
Antioxidant CA Supplier
SUNNOX® CA is a trisphenolic primary antioxidant with low volatility and good resistance to extraction. It protects polyolefins, wire and cable insulation, abdos, PVC, polyamide and rubber against long-term thermal oxidation.
CAS 1843-03-4 · Trisphenol · Primary antioxidant
- Lot de COA avec chaque expédition
- Des échantillons pour vos essais
- Support technique pour votre essai
Présentation du produit & avantages clés
Antioxidant CA (1,1,3-tris(2-methyl-4-hydroxy-5-tert-butylphenyl)butane) carries three hindered-phenol groups in one molecule, so it is efficient per unit weight and stays in the polymer at processing temperatures. It is used in PP and PE, composés de fils et de câbles, abdos, PVC, Pennsylvanie, hot-melt adhesives and rubber, and is normally combined with a phosphite such as 168 for processing stability.
Low volatility and extraction
Stays in the part at high processing temperatures and in contact with water.
Wire and cable use
Widely used in polyolefin insulation and jacketing compounds.
Spécifications techniques
| Paramètre | Valeur typique |
|---|---|
| Nom du produit | Antioxidant CA |
| Marque | SUNNOX® CA |
| Numéro CAS. | 1843-03-4 |
| Nom chimique | 1,1,3-Tris(2-methyl-4-hydroxy-5-tert-butylphenyl)butane |
| Formule moléculaire | C37H52O3 |
| Masse moléculaire | 544.8 |
| Apparence | Poudre blanche |
| Point de fusion | 185–190 °C |
| Matière volatile | ≤0,5% |
| Cendre | ≤0,1% |
Spécification typique. Chaque envoi est fourni avec un COA de lot; les limites applicables à votre commande sont confirmées dans le devis et le contrat.
Applications par polymère
Pick an application to see how CA is normally used and what to confirm before your trial.
Polyoléfines
Long-term thermal protection in PP and PE with a phosphite.
Vérifiez avant l'essai
- Resin grade and process (film, fibre, molding, tuyau)
- Processing temperature and number of passes
- Current antioxidant package and dosage
Fil & Cable Compounds
Used in polyolefin insulation and jacketing; ask about a metal deactivator if the compound contacts copper.
Vérifiez avant l'essai
- Cable standard and aging test
- Copper contact
- Current antioxidant package
abdos, PVC, Polyamide & Caoutchouc
Antioxidant for engineering plastics, PVC, hot-melts and rubber.
Vérifiez avant l'essai
- Polymer type
- Température de traitement
- Color requirement
Sélection & comparaison
Sélection d'un système antioxydant
| Votre exigence | Ce qui fonctionne habituellement |
|---|---|
| Stabilité de la couleur et de l'écoulement à l'état fondu pendant l'extrusion ou le moulage | Phosphite antioxydant secondaire (168) avec un primaire phénolique |
| Vieillissement thermique à long terme en service | Primaire phénolique à haut poids moléculaire (1010), souvent avec un thioester (DLTDP / DSTDP) |
| Couche mince, fibre, mélange à bas point de fusion | Phénolique à bas point de fusion (1076) pour une dispersion facile |
| Traitement répété / contenu recyclé | Relever la part de phosphite dans le mélange et vérifier le jaunissement après chaque passage |
| Stockage humide ou long transit | Phosphite résistant à l'hydrolyse tel que 168; garder les sacs scellés |
| Articles à contact alimentaire | Ask for the grade-specific food-contact statement before trials |
| Remplacement d'une note existante | Envoyez votre TDS ou COA actuel; we match on the parameters you approve |
Comparaison des antioxydants
Faites glisser ou faites défiler horizontalement pour voir toutes les colonnes →
| Produit | Taper | Mol. poids | Point de fusion | Emploi principal |
|---|---|---|---|---|
| SUNNOX® CA | Trisphenol · primary | 544.8 | 185–190 °C | Low-volatility long-term protection |
| SUNNOX® 1010 | Phénol encombré · primaire | 1177.6 | 110–125 °C | Protection thermique à long terme |
| SUNNOX® 330 | Phénol encombré · primaire | 775.2 | 240–245 °C | High-temperature, low-volatility protection |
| SUNNOX® 168 | Phosphite · secondaire | 646.9 | 183–187 °C | Stabilité du traitement, Couleur |
| SUNNOX® 3114 | Hindered phenol · isocyanurate | 784.1 | 218–223 °C | Low-extraction long-term protection |
Définissez les niveaux dans votre propre essai. Le bon niveau dépend de la résine, résidu de catalyseur, température de traitement et durée de vie. Les antioxydants primaires et secondaires effectuent des tâches différentes et ne sont pas interchangeables.
Emballage & stockage
Emballage
25 kg net bags or cartons with a PE inner liner. Palletized.
Stockage
Keep sealed in a cool, sec, ventilated place away from heat and direct sun. See the SDS for full handling details.
Délai de mise en œuvre & terms
Regular grades are usually in stock. For large volumes, lead time is confirmed in the quotation. We quote FOB and CIF.
Du premier e-mail à la fourniture approuvée
Name the failure you want to prevent
Yellowing or melt-flow change during processing points to the phosphite share; embrittlement or cracking after months in service points to the phenolic and thioester share. Note recycled content and the number of extrusion passes.
Start from a proven blend
Most polyolefin packages start from a phenolic primary plus a phosphite secondary, then adjust. Send your current package and we suggest a starting blend for the trial instead of changing several variables at once.
Comparez les chiffres qui comptent
For powders: essai, melting range, volatiles and light transmittance at 425/500 nm (a direct read on color). Ask for the same parameters on our COA that appear on your incoming-inspection sheet.
Lock in supply terms
Agree packaging, monthly volume, destination port and required documents up front. A matching CAS number alone does not qualify a new source; run your trial and keep the approved lot COA as the reference.
Dites-nous votre besoin. Nous correspondons à la note.
Start with your polymer, quantité et destination. Add your current grade or specification and we will quote against it.
| Information | Exemple |
|---|---|
| Polymer / Material | PP, PE, abdos, composé, mélange maître |
| Application | Injection molding, extrusion, film, fibre |
| Current additive | Grade or supplier you use today |
| Spécification requise | Your TDS, COA or key limits |
| Quantité | Commande à l'essai / mensuel / volume annuel |
| Emballage | Standard 25 kg or specific requirement |
| Destination | Pays et port |
| Documents nécessaires | COA, FDS, ATTEINDRE, food-contact statement |
Produits associés
SUNNOX® 1010
High-MW hindered phenolic primary antioxidant for long-term thermal protection with low volatility.
Voir le produit →SUNNOX® 330
High-melting phenolic antioxidant with very low volatility for high-temperature polyolefin and engineering-plastic use.
Voir le produit →SUNNOX® 168
Hydrolysis-resistant phosphite secondary antioxidant for color and melt-flow protection during processing.
Voir le produit →SUNNOX® 3114
Isocyanurate phenolic antioxidant with low extraction, used in polyolefin fiber, film and pipe.
Voir le produit →Antioxidant CA FAQ
CA or 1010?
Both are high-performance phenolics. CA is often chosen in wire and cable and where extraction resistance matters; 1010 is the general standard in polyolefins. Send your current grade and we match it.
How much SUNNOX® CA should I add?
Le niveau dépend de votre polymère, épaisseur de la pièce, autres additifs et conditions d'essai, alors mets-le dans ton propre essai. La TDS est disponible sur demande.
Is CA suitable for cable in contact with copper?
Copper accelerates oxidation; cable compounds in contact with copper usually also need a metal deactivator. Tell us the construction and we suggest a package.
Puis-je obtenir un échantillon avant de commander?
Oui. Tell us the polymer, the test you plan to run and the quantity you need. Samples ship with a COA so you can compare the lot against your current material.
Que se passe-t-il si un COA ne correspond pas à nos spécifications convenues ??
Send us the agreed specification and the COA showing the difference (parameter, unité et méthode de test). We check it with the production batch record before you accept the material, and replace or re-test where the lot is out of specification.